A two-component chemical resistant epoxy phenolic paint.
A two-component chemical resistant epoxy phenolic paint.
• High temperature resistant. Withstands continuous dry heat up to +200ºC. Discoloration possible. Suitable for immersion of hot water between +65ºC–90ºC. • Due to its binder type, Temaline EPL 100 has especially good resistance against many chemicals including light crude oil distillates, such as gasoline, diesel and kerosene. Resistance to fuels and chemicals are listed in the separate chemical resistance table. • Resistant to dilute solutions of non-oxidizing acids, alkali and salts in immersion. • Resistant to grey/waste water when applied 2x150µm. • As a CE marked product,Temaline EPL 100 is suitable for concrete surfaces.
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated. Note! Maximum dry film thickness is 1000 µm. The painting work should be performed and supervised according to 12944-7 if not otherwise stated in the respective technical data sheet. Excessive film thickness may result e.g. in cracking, sagging, prolonged drying time, soft film, less chemical resistance, gloss deviation, adhesion and intercoat functionality. In case the product is used otherwise than stated in the standard a written approval from Tikkurila is required.
Solventborne
Temaline EPL 100 withstands immersion in hot water up to +90°C and dry heat up to +150°C.
Due to its binder type, Temaline EPL 100 has especially good resistance against many chemicals including light crude oil distillates, such as gasoline, diesel and kerosene.
As a CE-marked product, Temaline EPL 100 is suitable for concrete surfaces.
You’re visiting Tikkurila website from United Kingdom. Would you like to visit the local UK site?
You can send to several people by separating multiple email addresses with commas.
Without the most up-to-date version of your browser, you may have problems using tikkurila.com website.
For instructions on how to upgrade, visit your browser's help resources: